TI–2.5CU

Common Name
Ti–2.5Cu
Ti 230
UNS
None assigned
General Information
Ti 230 combines the formability and weldability of unalloyed titanium with improved mechanical properties, particularly at elevated temperatures (up to 662°F (350°C)). The alloy may be used in the annealed condition as sheet, forgings and extrusions; it is used both in the airframe and in components such as bypass ducts for gas-turbine engines. Ageing can be used to raise the room temperature tensile properties by ~25% and nearly double the elevated temperature properties (eg creep @ 392°F(200°C)). Such a material is particularly attractive since it can be formed in the soft condition, thus lowering fabrication costs.
Common Specification
Specification Product Form
MSRR 8603 Sheet (Annealed)
MSRR 8602/8605 Forging stock, forgings
TA 58 Plate
TA52, MSRR8606 Sheet (SHT)
ASME SB-348 Bars and Billets
WL 3.7124, TA 53 Bar
Chemistry Requirements
N C H Fe O Cu Ti
0.03 0.08 0.01 0.20 0.20 2.0-3.0 Balance

% Maximum unless given as a range.

Minimum Tensile Properties
Condition UTS ksi (Mpa) >0.2%YS ksi (MPA) % El. % RA*
As specified (shape) 88 (610) 71 (490) 10 25
Typical Tensile Properties
Condition UTS ksi (Mpa) >0.2%YS ksi (MPA) % El. % RA*
Sheet ST 90 (620) 77 (530) 24 (on 2″(50mm))
Sheet STA 175-185 (1207-1276) 96 (660) 20 (on 2″(50mm))
Bar & Rod ST 91 (630) 72 (500) 27 45
Bar & Rod STA 107 (740) 84 (580) 22 41
Extrusions ST 91 (630) 72 (500) 30 40
Extrusions STA 115 (790) 97 (670) 28 30

 
Note: Typical properties are not to be utilized as a requirement, but are only listed for guidance. These properties may or may not be attainable in all circumstances.
* %Ra not required by all specifications
 
Trademark Notice: Some names are trade names and/or trademarks of specific manufacturers. Titan Singapore is not affiliated with any manufacturer(s). Orders will be filled to meet specifications from any available source(s). Names are listed solely for reference to help identify products consistent with listed specifications.